industrial repair agent > high temperature aluminum rebuilding repair agent compound

high temperature aluminum rebuilding repair agent compound

BD118 high temperature aluminum rebuilding epoxy compound repair agent

Product description:
It’s the high temperature high performance polymerization metal materials compounded by various alloy material and
modified toughening heat resistant resin.The highest temperature resistance is 300℃,suitable for the repairing of
various aluminum casting defect and aluminum parts wear under the high temperature working condition.
The color after repairing is basically the same as the substrates,with the very high strength and excellent wear&corrosion
resistance and aging resistant properties,can do various mechanical processing together with substrates.

product index of our BD118 high temperature aluminum metal rebuilding compound repair agent:

product name	physical state	standard packaging	volume (cm3)	operational time limit (25℃)	usable time (25℃)
BD118 high temperature aluminum repair agent rebuilding compound	paste	250g/set Two-component	178	45min	24h

color	density (g/cm3)	compressive strength (Mpa) GB1041-2008	shear strength (Mpa) GB7124-2008	bending strength (Mpa) GB1042-1999	hardness （Shore D） ASTM-D-2556	working temperature （℃）
aluminum	1.41	97	15	47	89	-60～250

How to use:
1.Surface treatment: Do the coarsening treatment on the pending-repair or needing-bonding area,then clean it by cleaning agent.

2.Configuration: According to the mass ratio A:B=4:1 or volume ratio A:B=4:1, make A and B two components mix uniformly,
then use it up within specified operation time limit.

3.Coating: Make the mixed-up material spread coating on the pending-repair areas layer by layer,the first layer should be compacted,make it infiltrate fully with the substrates.
If the following working procedure needs machining,should keep out appropriate machining allowance

4.Curing: cure for 2 hours at the temperature of 25～30℃,heat it up to the temperature of 80℃ and keep this temperature for 2 hours or cure for 24 hours at the temperature of 25～30℃ before using,if the temperature is low,should heat it up or prolong the curing time to promote the curing.

Packaging specification:
Two-component,250g/set,8 sets/carton or 16 sets/carton.

Transportation storage:
Sealed storage in the cool and dry place.The warranty period is 12 months.Avoid placing it upside down,
knocking against and transporting it as a non-dangerous product during transportation.

Product packaging photo of BD118 metal aluminum high temperature resistant epoxy repair putty paste two parts compound: